Home > Product introduction > Cross linking agent, functional resin>
Golf Ball Cross-linking agent |
 |
|
| |
 |
 |
 |
 |
Increase the modulus of elasticity, strength, durability when processing golf ball |
|
Low compression coagulation and increase in productivity through reduction of hardening time |
|
Improved work environment by minimizing generation of dust while mixing rubber |
|
Water content rate is low with less than 0.3%, and it can be used clearly in the field without 2nd pulverization process |
|
Maintenance of the consistent emission pressure and superb processing ability when golf ball core is formed |
|
|
|
 |
 |
Zinc Diacrylate : ZDA-12, ZDA-8 |
|
|
| |
| JINJEIL-ZDA is the cross linking agent that can be used in various areas, developed especially for the compression, injection and transport of molded objects. In particular, it is a highly functional plasticizer that is characterized by elasticity modulus, high strength and durability, low compression coagulation, reduction of the hardening time and the amount of raw materials injected in the golf ball industry. JINJEIL-ZDA significantly curtails generation of dust when mixing rubber, and ensures that the dust does not get adhered to Banbury mixer which in turn increases golf ball productivity. |
| |
| Chemical Information |
| |
Zinc Diacrylate |
| Chemical Name |
Zinc di(2-propenate) |
| Structure |
(CH2=CHCOO)2Zn |
| MF
| C6H6O4Zn |
| MW |
207.5 |
| TCSA(RN) |
14643-87-9 |
| Einecs |
238-692-3 |
|
| |
| Quality Standards and Properties of samples Measurements Result
|
| ITEM |
SPECIFICATION |
RESULT |
K.S.M |
Appearance
|
WHITE POWDER
|
WHITE POWDER |
Visual Judgement |
| Specific Gravity (25℃) |
1.6 ± 0.1 |
1.553 |
6634 |
| Moisture (wt%) |
MAX. 0.3
|
0.265
|
ISO 760 |
| Ash (wt%) |
36 ± 2
|
36.23
|
6634 |
| Metal content(wt%) |
29 ± 1
|
28.86
|
5202 |
| Acrylate Content (wt%) |
52 ± 2 |
51.5 |
5000 |
|
| |
|
 |
ZDMA (Zinc dimethacrylate) |
 |
CDA (Calcium Diacrylate) |
 |
MDA (Magnesium Diacrylate) |
 |
ZST (Zinc Stearate) |
※ Various products are produced and supplied. Therefore, it can be used to perform excellent functions when producing golf ball.
|
|
| |
|
|
| |
 |
|
Excellent quality is recognized and the product is exported to all over the world (China, Taiwan, India, USA, Malaysia, Indonesia etc.) |
|
Focused supply of all the golf balls produced at the world-class Golf Maker and TaylorMade |
|
|
|
|
|